Micro Structure
Tradename: Tough Pitch with Ag (STP)
Material No. UNS System (ASTM): C11600
Chemical Composition
| Element | ||
|---|---|---|
| Cu(1,2,3) | Ag(4) | |
| Min (%) | 99.90 | 0.085 |
- This is a high conductivity copper which has, in the annealed condition a minimum conductivity of 100% IACS.
- Cu value includes Ag.
- Oxygen and trace elements may vary depending on the process.
- Ag 0.085% min is the equivalent of, Ag 25 Troy Oz min.
Mechanical Properties
| Form | Tensile Strength In Mpa | Elongation In % | Rockwell B Scale - HRB |
|---|---|---|---|
| Rod | 310-379 | 20-10 | 45-60 |
| Flat Products | 248-345 | 40-6 | 10-50 |
Physical Properties
| Melting Point –Liquidus °C | 1082 |
| Density lb/cu in. at 20°C | 0.322(1) |
| Specific Gravity | 8.91(2) |
| Electrical Conductivity% IACS at 20°C | 100 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °C at 20°C | 224 |
| Coefficient of Thermal Expansion 20-300 10⁻⁶ per °C (200 – 300°C) | 9.8 |
| Specific Heat Capacity Btu/ lb /°C at 20°C | 0.092 |
| Modulus of Elasticity in Tension ksi | 17000 |
| Modulus of Rigidity ksi | 6400 |
| (1) Actual value is .321 - .323. (2) Actual value is 8.89 - 8.94. |
|
Thermal Properties
| Treatment | Minimum* | Maximum* |
|---|---|---|
| Annealing | 482 | 760 |
| Hot Treatment | 760 | 871 |
| * Temperature is Measured in Celsius. | ||
Fabrication Properties
| Technique | Stability |
|---|---|
| Brazing | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Coated Metal Arc Welding | Not Recommended |
| Forgeability Rating | 65 |
| Gas Shielded Arc Welding | Fair |
| Machinability Rating | 20 |
| Oxyacetylene Welding | Not Recommended |
| Seam Weld | Not Recommended |
| Soldering | Excellent |
| Spot Weld | Not Recommended |
General Fabrication Processes
- Forging
- Extruding
- Drawing
- Machining
Applicable Form
| Form | Description |
|---|---|
| Rod | Hot Extruded & Cold Drawn Copper Rod |
| Flat | Hot Extruded & Cold Drawn Copper (COPPER BUS BAR, Flat BAR ,Strips) |
| Tube | Hot Extruded Tube |
Typical Uses / Application
| Product Category | Product | Reason |
|---|---|---|
| Electrical | Busbars | Electrical Conductivity |
| Commutator Bars and Segments | Electrical Conductivity | |
| Contacts | Electrical Conductivity, Corrosion Resistance | |
| Generator Coils | Electrical Conductivity | |
| Radio Parts | Electrical Conductivity | |
| Switches | Electrical Conductivity | |
| Terminals | Electrical Conductivity | |
| Windings | Electrical Conductivity | |
| Industrial | Clad Metals | Electrical Conductivity |
Other Products
-
Copper Berylium
Alloy Grade - CuBe -
Copper Chromium
Alloy Grade - CuCr -
Copper Chromium Zirconium
Alloy Grade - CuCrZr -
Copper – ETP
Alloy Grade - Cu-ETP -
Copper – HCP
Alloy Grade - Cu-HCP -
Copper Nickel
Alloy Grade - CuNi -
Copper Zirconium
Alloy Grade - CuZr -
Silver Bearing Copper
Alloy Grade - CuAg -
Silicon Bronze
Alloy Grade - CuNi2Si
Copyrights © 2019 Modison Copper Pvt Ltd | All Rights Reserved.
Site By Spenta Digital